A resina Honam H5300 é um PP homopolímero de boa processabilidade.
Aplicações TípicasA resina Honam H5300 é recomendada para ráfia e monofilamentos ( sacos e cordas).
Fabricante
Honam Petrochemical
Índice de Fluidez [ 2,16 Kg / 230°C ] - g/10 min / Densidade - g/cm³
3,5 / 0,9
Contra Tipos Índice de Fluidez [ 2,16 Kg / 230°C ] - g/10 min / Densidade - g/cm³
| KY 6110 (Quattor) | 3,0 / 0,905 |
| H503 (Braskem) | 3,5 / 0,905 |
| HP 550K (Quattor) | 3,5 / 0,905 |
| KY 6900 (Quattor) | 3,5 / 0,905 |
Para baixar as especificações técnicas do fabricante cliqe aqui! 
F00952 resin is recommended for blown film extrusion. This product is
suggested for the manufacture of high strength grocery sacks, shopping bags
and high quality thin films for multi wall sack liners and replacement for thin
paper products. Films of this product are readily treated and printed to give
high quality graphics.
Physical Properties Unit Value(1) ASTM Method
Melt index g/10 min. 0.05 D-1238
HLMI (2) g/10 min. 9 D-1238
Density g/cm3. 0.952 D-1505
Vicat softening point °C 125 D-1525
Film Properties *
1% Secant modulus
MD
TD
MPa
1250
1500
D-882
Tensile strength @yield
MD
TD
MPa
33
31
D-882
Tensile strength
@break
MD
TD
MPa
60
56
D-882
Tensile elongation
@break
MD
TD
%
400
550
D-882
Elmendorf tear strength
MD
TD
g
12
60
D-1922
Dart Impact, F50 g 180 D-1709
*The film properties have been measured on F00952 (15 μ film, 4:1 blow-up ratio)
(1) Typical values should not be construed as specification limits.
(2) High Load Melt Index has been found to be more accurate reference for F01552.
Processing Conditions
suggested for the manufacture of high strength grocery sacks, shopping bags
and high quality thin films for multi wall sack liners and replacement for thin
paper products. Films of this product are readily treated and printed to give
high quality graphics.
Physical Properties Unit Value(1) ASTM Method
Melt index g/10 min. 0.05 D-1238
HLMI (2) g/10 min. 9 D-1238
Density g/cm3. 0.952 D-1505
Vicat softening point °C 125 D-1525
Film Properties *
1% Secant modulus
MD
TD
MPa
1250
1500
D-882
Tensile strength @yield
MD
TD
MPa
33
31
D-882
Tensile strength
@break
MD
TD
MPa
60
56
D-882
Tensile elongation
@break
MD
TD
%
400
550
D-882
Elmendorf tear strength
MD
TD
g
12
60
D-1922
Dart Impact, F50 g 180 D-1709
*The film properties have been measured on F00952 (15 μ film, 4:1 blow-up ratio)
(1) Typical values should not be construed as specification limits.
(2) High Load Melt Index has been found to be more accurate reference for F01552.
Processing Conditions